Category | Polymer , Thermoplastic , Polypropylene (PP) |
Manufacturer | Azdel |
Trade Name | SuperLite® |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (2 mm Molded Thickness).pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.570 g/cc | 0.570 g/cc | ASTM D3574 |
Filler Content | 55 % | 55 % | ASTM D5630 |
Thickness | 6000 - 6500 microns | 236 - 256 mil | Typical free lofted thickness after heating |
Linear Mold Shrinkage | <= 0.00020 cm/cm | <= 0.00020 in/in | Typical, molds cut to zero |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 34.0 MPa | 4930 psi | ASTM D638 |
Tensile Modulus | 3.80 GPa | 551 ksi | ASTM D638 |
Flexural Strength | 24.5 MPa | 3550 psi | SAE J949 |
Flexural Modulus | 1.90 GPa | 276 ksi | SAE J949 |
Impact | 660 | 660 | Multi-axial in Newtons, at 23°C, at max. load, measured on flat plaques; ASTM D3763 |
Impact Test | 3.00 J @Temperature 23.0 °C |
2.21 ft-lb @Temperature 73.4 °F |
Multi-axial, at max. load; ASTM D3763 |
5.20 J @Temperature 23.0 °C |
3.84 ft-lb @Temperature 73.4 °F |
Multi-axial, at failure, measured on flat plaques; ASTM D3763 |
Descriptive Properties | Value | Comments |
---|---|---|
Available Colors | Natural and Charcoal | |
Draw Ratio | Max 1.5:1 |