Ashley Polymers Ashlene® P292 PPO
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Impact Grade |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® P292 PPO.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion grade, highest heat deflection temperature and good impact strength.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | ATSM D638 |
| Flexural Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Izod Impact, Notched | 2.55 J/cm | 4.78 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 315 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion 8700A Polyvinyl Chloride, Rigid (PVC, Rigid)
- Polyplastic TechnoTep B® 65 A Thermoplastic Elastomer, Mineral Filled
- Kingfa PBT-T30 30% Mineral Filled PBT
- H.C. Starck Grade AX 10 Silicon Metal Powder Si
- Tipco Tipcolite® TX 211 Phenolic Compound, Wood Flour, having Medium Flow & High Electrical Properties
- Eurotec® Tecomid® NA40 GR15 GR003 XA70 PA6.6, 15% glass fiber reinforced, flame retardant - halogen free (RoHS compliant), heat stabilized, grey RAL 7035
- Bales Mold Service Ni-Hard® (Nickel-Cobalt) Mold Coating
- Aaron Industries AAROPRENE® TFPP 2010 Talc Filled Polypropylene
- 3M N200NT Adhesion Promoter
- Ascend Performance Materials Vydyne® M344 Nylon 66/6, ignition resistant, DAM
Copyright © lookpolymers.com All Rights Reserved