Ashley Polymers Ashlene® P114 PBT Polyester
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® P114 PBT Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A high impact polyester with low shrinkage.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | ASTM D638 |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Izod Impact, Notched | 5.30 J/cm | 9.93 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8955 (UF) Synthetic Oil
- Karina E Micro-Ex 6536/212 Brown PVC Compound
- Solvay ANTAROX® FD 36 Surfactant
- Polyplastics Freqtis® C0511A (PPS/LCP), Molding Compound
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR Thanecure® ZM
- A. Schulman POLYBATCH™ Red 5505 Concentrate Based In Polyethylene
- BASF Ultramid® C33 LN 0.025 mm Blown Film PA6/66
- Arlon 90B32R016AC Aluminum Clad Press Pad with "C-Finish"
- Polykemi AB POLYfill PPH T8030 Polypropylene Homopolymer, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved