Hexcel® HexPly® 954-2A Curing Cyanate Resin, S-2 Glass Fiber Reinforced 8 Harness Satin Fabric

Category Polymer , Thermoset , Epoxy
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Hexcel® HexPly® 954-2A Curing Cyanate Resin, S-2 Glass Fiber Reinforced 8 Harness Satin Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 627 MPa
<br>@Temperature 23.0 °C
 90900 psi
<br>@Temperature 73.4 °F
 0°
Elongation at Yield 2.8 %
<br>@Temperature 23.0 °C
 2.8 %
<br>@Temperature 73.4 °F
Tensile Modulus 28.3 GPa
<br>@Temperature 23.0 °C
 4100 ksi
<br>@Temperature 73.4 °F
 0°
Flexural Yield Strength 848 MPa
<br>@Temperature 23.0 °C
 123000 psi
<br>@Temperature 73.4 °F
Flexural Modulus 28.3 GPa
<br>@Temperature 23.0 °C
 4100 ksi
<br>@Temperature 73.4 °F
Compressive Yield Strength 317 MPa
<br>@Temperature 163 °C
 46000 psi
<br>@Temperature 325 °F
 0°, Wet
345 MPa
<br>@Temperature 149 °C
 50000 psi
<br>@Temperature 300 °F
 0°, Wet
365 MPa
<br>@Temperature 204 °C
 52900 psi
<br>@Temperature 399 °F
 0°
379 MPa
<br>@Temperature 191 °C
 55000 psi
<br>@Temperature 376 °F
 0°
427 MPa
<br>@Temperature 177 °C
 61900 psi
<br>@Temperature 351 °F
 0°
434 MPa
<br>@Temperature 163 °C
 62900 psi
<br>@Temperature 325 °F
 0°
586 MPa
<br>@Temperature 23.0 °C
 85000 psi
<br>@Temperature 73.4 °F
Compressive Modulus 29.0 GPa
<br>@Temperature 191 °C
 4210 ksi
<br>@Temperature 376 °F
 0°
29.6 GPa
<br>@Temperature 163 °C
 4290 ksi
<br>@Temperature 325 °F
 0°
29.6 GPa
<br>@Temperature 204 °C
 4290 ksi
<br>@Temperature 399 °F
 0°
29.6 GPa
<br>@Temperature 23.0 °C
 4290 ksi
<br>@Temperature 73.4 °F
31.0 GPa
<br>@Temperature 177 °C
 4500 ksi
<br>@Temperature 351 °F
 0°
Shear Strength 35.2 MPa
<br>@Temperature 163 °C
 5110 psi
<br>@Temperature 325 °F
 Short Beam, Wet
37.2 MPa
<br>@Temperature 204 °C
 5400 psi
<br>@Temperature 399 °F
 Short Beam
37.2 MPa
<br>@Temperature 149 °C
 5400 psi
<br>@Temperature 300 °F
 Short Beam, Wet
41.4 MPa
<br>@Temperature 177 °C
 6000 psi
<br>@Temperature 351 °F
 Short Beam
43.4 MPa
<br>@Temperature 191 °C
 6290 psi
<br>@Temperature 376 °F
 Short Beam
52.4 MPa
<br>@Temperature 163 °C
 7600 psi
<br>@Temperature 325 °F
 Short Beam
75.2 MPa
<br>@Temperature 23.0 °C
 10900 psi
<br>@Temperature 73.4 °F