- Asahi Kasei Thermylene® P6-15FG-1734 15% Glass Fiber Reinforced, Heat Stabilized
Asahi Kasei Thermylene® P6-15FG-1734 15% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P6-15FG-1734 15% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.01 g/cc | 1.01 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Melt Flow | 8.5 g/10 min | 8.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 84 | 84 | ASTM D785 |
| Tensile Strength, Yield | 49.6 MPa | 7200 psi | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.48 GPa | 360 ksi | ASTM D638 |
| Flexural Strength | 67.6 MPa | 9800 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 1.44 J/cm | 2.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 54.0 µm/m-°C @Temperature 20.0 °C |
30.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 285 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Quadrant EPP Ketron® CM GF30 Compression Molded, 30% Glass Reinforces Polyethererther Ketone(ASTM Product Data Sheet)
- NOVA Chemicals Surpass® FPs117-C Octene Copolymer sLLDPE Film Resins
- MTI ThermoStran® PP-30C Long Carbon Fiber Compound
- SABIC Innovative Plastics LNP LUBRILOY D20009 PC
- Zeon Chemicals Zeonex® RS420 Cyclo-Olefin Polymer
- Dow Corning 431 HS RESIN
- 3M Bumpon™ SJ5904 Resilient Rollstock
- ATI Wah Chang Vanadium
- Momentive Performance Materials TUFEL™ II 94606 Low Volatile Extrusion Heat Cured Rubber
- Total Finaprene® 401 Styrene-Butadiene TPE Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved