Braskem BS002HS HDPE Blow Molding Polyethylene Copolymer

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer Braskem
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem BS002HS HDPE Blow Molding Polyethylene Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resin BS002HS is a high-density polyethylene, bimodal copolymer. It presents good rigidity, good impact resistance, and good reproducibility of the weight of the bottles. It also has excellent environmental stress cracking resistance and excellent regularity and uniformity in processing. It is used in bottles for cleaning products, food products, surface-active agents, and cosmetics.
Physical Properties Metric English Comments
Density 0.957 g/cc
0.0346 lb/in³
ASTM-D792
ESCR 100% Igepal® 220 hour

@Thickness 2.00 mm,
Temperature 50.0 °C
220 hour

@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
ESCR 10% Igepal® 60 hour

@Thickness 2.00 mm,
Temperature 50.0 °C
60 hour

@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
Melt Flow 0.35 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.35 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
24 g/10 min

@Load 21.6 kg,
Temperature 190 °C
24 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM-D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 62
62
ASTM-D2240
Tensile Strength at Break 35.0 MPa
5080 psi
ASTM-D638
Tensile Strength, Yield 30.0 MPa
4350 psi
ASTM-D638
Flexural Modulus, 1% Secant 1110 MPa
161000 psi
ASTM-D790
Izod Impact, Notched 2.57 J/cm
4.81 ft-lb/in
ASTM-D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 71.0 °C
160 °F
ASTM-D648
Vicat Softening Point 128 °C

@Load 1.02 kg
262 °F

@Load 2.25 lb
ASTM-D1525