Arlon 0.011" (0.2794 mm) Uncured Silicone Traction Motor Insulation (P29600R011)

Category Polymer , Thermoset , Silicone
Manufacturer Arlon
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 0.011" (0.2794 mm) Uncured Silicone Traction Motor Insulation (P29600R011).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
0.006 in., +0.002, -0.001(0.2 mm, +0.05, -0.03) uncured silicone on 0.005 in. (0.08 mm) nominal PTFE coated fiberglass; 0.0015 in. (0.038 mm) polyethylene interleave; overall thickness 0.011 in ±0.001(0.3 mm ± 0.03). The shelf life is defined as the duration of time for which the product will meet the physical requirements outlined below. It does not guarantee the product’s usefulness in all applications. Color: Red. Weight: 381.4 g/m² ± 33.9 (11.25 oz./yd.² ± 1.0). Shelf Life: 6 months from date of manufacture at 23.8°C (75°F). Cure Time: 0.25 hours. Post Cure: 204°C (400°F), for 2 hours.Information provided by the manufacturer, Arlon Silicone Technologies Division.
Mechanical Properties Metric English Comments
Hardness, Shore A 55 - 65
55 - 65
Tensile Strength, Ultimate >= 6.20 MPa
>= 899 psi
Elongation at Break >= 200 %
>= 200 %
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 260 °C
500 °F
Minimum Service Temperature, Air -56.6 °C
-69.9 °F
Electrical Properties Metric English Comments
Dielectric Strength >= 17.0 kV/mm
>= 432 kV/in
Processing Properties Metric English Comments
Processing Temperature 176.6 °C
349.9 °F
curing temp., at 0.345 MPa (50 psi)