Arkema Group Rilsan® BZM 43 G9 Nylon 11, 43% Glass Fiber Filled (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11 with 40% Glass Fiber Filler
Manufacturer	Arkema
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Rilsan® BZM 43 G9 Nylon 11, 43% Glass Fiber Filled (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Designation ISO 1874-PA11,MS,18-080,(G+C)(F+D)(45+05)Rigid grade with glass fiber (43%) and graphite filler for injection molding. Available color: steel black gray. Additive free.High rigidity. High compressive strength. Low friction coefficient. Abrasion resistance. Low linear expansion coefficient. Low shrinkage: include 0,5% on average for the design of the mold. High dimensional stability.Example applications: Mechanical parts with friction such as gear or bearing.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English
Density	1.42 g/cc	0.0513 lb/in³
Water Absorption	1.1 %	1.1 %
Melt Flow	2.2 g/10 min @Load 2.16 kg, Temperature 235 °C	2.2 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	146 MPa	21200 psi	5 mm/min
Elongation at Break	4.0 %	4.0 %	5 mm/min
Tensile Modulus	12.4 GPa	1800 ksi	1 mm/min
Charpy Impact Unnotched	6.69 J/cm²	31.8 ft-lb/in²
	7.50 J/cm² @Temperature -30.0 °C	35.7 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	1.21 J/cm²	5.76 ft-lb/in²
	1.02 J/cm² @Temperature -30.0 °C	4.85 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
Melting Point	183 °C	361 °F	10°C/min
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.10 mm	HB @Thickness 0.122 in