Arkema Group Rilsan® BZM 23 G9 Nylon 11, 23% Glass Fiber Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11 with 20% Glass Fiber Filler |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® BZM 23 G9 Nylon 11, 23% Glass Fiber Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 1874-PA11,MS,18-040,(G+C)(F+D)(25+05)Rigid grade with glass fiber (23%) and graphite filler for injection molding. Available color: steel black gray. Additive free.Rigidity. Low friction coefficient. Abrasion resistance. High compressive strength. Low linear expansion coefficient. Low shrinkage: include 0,5% on average for the design of the mold. High dimensional stability.UL classification: UL94 HB RTI(C) 65/65/65Example applications: Mechanical parts with friction such as gear or bearing.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | |
| Water Absorption | 1.2 % | 1.2 % | |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 235 °C |
2.2 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5 mm/min |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min |
| Tensile Modulus | 7.69 GPa | 1120 ksi | 1 mm/min |
| Charpy Impact Unnotched | 7.80 J/cm² | 37.1 ft-lb/in² | |
| 8.49 J/cm² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.27 J/cm² | 6.04 ft-lb/in² | |
| 0.940 J/cm² @Temperature -30.0 °C |
4.47 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 183 °C | 361 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.10 mm |
HB @Thickness 0.122 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dissipation Factor | 0.00046 @Frequency 1e+6 Hz |
0.00046 @Frequency 1e+6 Hz |
|
| 0.000517 @Frequency 100 Hz |
0.000517 @Frequency 100 Hz |
Users viewing this material also viewed the following:
- MV Labs K150 KNaC4H4O6.xH2O Potassium sodium tartrate tetrahydrate
- SABIC Innovative Plastics Lexan® EXL8454 PC COPOLYMER (Asia Pacific)
- Menzolit Menzolit® BMC 0160 Unsaturated Polyester UP
- SABIC Innovative Plastics ULTEM 2200R PEI (Asia Pacific)
- Polyplastics Duracon® AW-01 Acetal Co-polymer (POM), High sliding, Special lubricant, High sliding
- Chengdu Polyster H4543 Thermoplastic Polyether-ester Elastomer (TPEE)
- EMS-Grivory Grivory® L 20 L PA12
- BASF Styropor® P 340 EPS
- Asia International Enterprise (Hong Kong) 60G7F Nylon 66, 35% Filled
- ArcelorMittal FB 590 Hot rolled ferrite-bainite steel
Copyright © lookpolymers.com All Rights Reserved