Arkema Group Rilsan® BMV 400 TL Nylon 11 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11, Unreinforced
Manufacturer Arkema
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® BMV 400 TL Nylon 11 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA11,M,18-002,ZFlexible grade for injection molding. Available color: natural. Light and heat stabilized. Plasticizing agent free.Outstanding impact strength and tear spreading at low temperature. Good abrasion resistance. Low shrinkage: include 1% on average for the design of the mold. Good dimensional stability (low moisture absorption).Example applications: Mechanical parts with impact and vibrations resistance.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.00 g/cc
0.0361 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Yield 15.0 MPa
2180 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 34 %
34 %
50 mm/min
Tensile Modulus 0.185 GPa
26.8 ksi
1 mm/min
Charpy Impact Unnotched NB
NB
NB
NB
Low Temp
Charpy Impact, Notched NB
NB
2.37 J/cm²

@Temperature -30.0 °C
11.3 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C

@Temperature 20.0 °C
61.1 µin/in-°F

@Temperature 68.0 °F
Melting Point 175 °C
347 °F
(Dry)
Deflection Temperature at 0.46 MPa (66 psi) 70.0 °C
158 °F
Deflection Temperature at 1.8 MPa (264 psi) 45.0 °C
113 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in