Arkema Group Rilsan® AUM 50 NOIR T6LD Nylon 12, 50% Glass Bead Filled (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Glass Bead Filled
Manufacturer	Arkema
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Rilsan® AUM 50 NOIR T6LD Nylon 12, 50% Glass Bead Filled (Dry).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Designation ISO 1874-PA12,MHLR,16-020,GB50Rigid grad with glass beads filler (50%) for injection molding. Available color: black. Reinforced light and heat stabilizing agents. Mold-release agent.Good mechanical properties. Reinforced isotropic performances. High compressive strength. Very low shrinkage: include 0,5% on average for the design of the mold. High dimensional stability (low moisture absorption). Low coefficient of linear expansion.Potable water contact approval WRC 950 1509.Example applications: Mechanical parts with dimensional precision.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English
Density	1.42 g/cc	0.0513 lb/in³
Water Absorption	1.0 %	1.0 %
Melt Flow	5.0 g/10 min @Load 2.16 kg, Temperature 235 °C	5.0 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	52.0 MPa	7540 psi	50 mm/min
Elongation at Break	18 %	18 %	Nominal Strain; 50 mm/min
Elongation at Yield	4.0 %	4.0 %	50 mm/min
Tensile Modulus	3.64 GPa	528 ksi	1 mm/min
Charpy Impact Unnotched	8.11 J/cm²	38.6 ft-lb/in²
	7.60 J/cm² @Temperature -30.0 °C	36.2 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	0.420 J/cm²	2.00 ft-lb/in²
	0.350 J/cm² @Temperature -30.0 °C	1.67 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
Melting Point	174 °C	345 °F	10°C/min
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.10 mm	HB @Thickness 0.122 in

Electrical Properties	Metric	English	Comments
Dissipation Factor	0.000423 @Frequency 1e+6 Hz	0.000423 @Frequency 1e+6 Hz
	0.00053 @Frequency 100 Hz	0.00053 @Frequency 100 Hz