Arkema Group Rilsan® 8020 Nylon 11, Flexible Tubing Grade (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11, Flexible Tubing Grade |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® 8020 Nylon 11, Flexible Tubing Grade (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 1874-PA11/xx,E,16-003Transparent and flexible copolymer for tubes extrusion. Additive free.Good flexibility. Very good transparency. High chemical resistance.USP XXIII class VI approval. Food contact approval EEC directive N 90/128. Example applications: Beer tubing, catheters.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 235 °C |
14 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 28 % | 28 % | 50 mm/min |
| Tensile Modulus | 0.405 GPa | 58.7 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | NB | NB | |
| 1.22 J/cm² @Temperature -30.0 °C |
5.81 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 171 °C | 340 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 °C | 104 °F | |
| Vicat Softening Point | 180 °C | 356 °F | 50°C/hr; 50N |
| Flammability, UL94 | V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | |
| Surface Resistance | 4.00e+14 ohm | 4.00e+14 ohm | |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Valox® 420SE0 PBT
- STAR Thermoplastic Alloys & Rubbers StarFlex® P 7330-9000 TPE
- A. Schulman POLYBATCH™ Yellow 2600V Concentrate Based In Polyethylene
- Ensinger Tecapeek® XP-104 Compression Molded PEEK Compound, with 7% Molybdenum Disulfide, 3% PTFE and 25% Carbon Fiber
- Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (2.5 mm Molded Thickness)
- Alliance BCN-13 Bonded (Composite) Magnetic Material
- BCC Products BC 100 Medium Cyanoacrylate Adhesive
- Arkema Group Oroglas® V 045 Acrylic, Extrusion Grade (discontinued **)
- Eastman E6838-975F Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved