Honeywell Capran® Oxyshield™ OMBS (0.60 mil) Monoaxially Oriented, Co-Extruded Nylon6/EVOH/Nylon 6 Clear Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade |
| Manufacturer | Honeywell |
| Trade Name | Capran® Oxyshield™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Oxyshield™ OMBS (0.60 mil) Monoaxially Oriented, Co-Extruded Nylon6/EVOH/Nylon 6 Clear Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Oxyshieldâ„¢ Oriented Medium Barrier is a 0.60 mil (15 micron) monoaxially oriented, coextruded nylon 6/EVOH/nylon 6 clear film with slip additive having excellent gas barrier through moderate relative humidity. The film provides high strength, good chemical resistance, and excellent flavor and aroma barrier for food packaging. Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0410 lb/in³ | Yield Density |
| Water Vapor Transmission | 217 g/m²/day | 14.0 g/100 in²/day | 100°F (37.8°C) / 100%RH; ASTM F1249 |
| Oxygen Transmission Rate | 3.10 cc/m²/day | 0.200 cc/100 in²/day | 73°F (23°C) / 65%RH; ASTM D3985 |
| Thickness | 15.2 microns | 0.600 mil | |
| Surface Tension | >= 56 dynes/cm | >= 56 dynes/cm | treated side; ASTM D2578 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, TD | 66.2 - 75.8 MPa | 9600 - 11000 psi | ASTM D882 |
| Film Elongation at Break, MD | 60 - 85 % | 60 - 85 % | ASTM D882 |
| Film Elongation at Break, TD | 260 - 440 % | 260 - 440 % | ASTM D882 |
| Secant Modulus, MD | 2.586 - 3.516 GPa | 375.1 - 510.0 ksi | ASTM D882 |
| Secant Modulus, TD | 2.413 - 2.896 GPa | 350.0 - 420.0 ksi | ASTM D882 |
| Coefficient of Friction | 0.18 - 0.35 | 0.18 - 0.35 | film to stainless steel; ASTM D1894 |
| 0.47 - 0.91 | 0.47 - 0.91 | film to film; ASTM D1894 | |
| Tear Strength Test | 1000 - 1600 | 1000 - 1600 | graves tear TD, grams/mil; ASTM D1004 |
| 1100 - 1650 | 1100 - 1650 | graves tear MD, grams/mil; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 269 - 379 MPa | 39000 - 55000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 62.1 - 103 MPa | 9000 - 15000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | <= 10 % | <= 10 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| Shrinkage, TD | <= 1.5 % | <= 1.5 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 5.5 % | <= 5.5 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
Users viewing this material also viewed the following:
- Lotte Chemical Titan TITANEX® LF1044 Linear low density polyethylene resin (discontinued **)
- Overview of materials for Polyphenylene Sulfide (PPS); Molded
- SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10 (Asia Pacific)
- Solvay Specialty Polymers Galden® D03 PFPE Fluid
- Zeon Chemicals Zetpol® ZCS 2395 Hydrogenated Nitrile Elastomomer
- Hexcel® HexForce™ 332 Fiber Glass Fabric
- Constellium Planoxal® 50 Aluminum plate
- Alloy Wire International RW 80 Ni-Cr Resistance Wire
- A. Schulman POLYBATCH™ Metallic Grey 80330/2
Copyright © lookpolymers.com All Rights Reserved