Arkema Group Pebax® 4033 Polyether Block Amide (PEBA)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyether Block Amide (PEBA) |
| Manufacturer | Arkema |
| Trade Name | Pebax® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Pebax® 4033 Polyether Block Amide (PEBA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical application: Mechanical partsInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hr in water at 20°C; ASTM D570 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | 20°C and 65% RH; ASTM D570 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 42 | 42 | ASTM D2240 |
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | 450 % | 450 % | ASTM D638 |
| Modulus of Elasticity | 0.0500 GPa | 7.25 ksi | ASTM D638 |
| Flexural Modulus | 0.0840 GPa | 12.2 ksi | ASTM D790 |
| Resilience | 0.625 | 0.625 | BS 903 par: A 8 |
| Flex Crack Resistance | 2.0 | 2.0 | [mm] 20°C / 100000 flexures; ASTM D813 |
| 4.5 | 4.5 | [mm] -20°C / 50000 flexures; ASTM D813 | |
| Izod Impact, Notched | NB | NB | ASTM D256-A |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ASTM D256-A | |
| Izod Impact, Unnotched | NB | NB | ASTM D256-A |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ASTM D256-A | |
| Tear Strength | 70.0 kN/m | 399 pli | notched; ASTM D624 (C) |
| 95.0 kN/m | 542 pli | unnotched; ASTM D624 (C) | |
| Taber Abrasion, mg/1000 Cycles | 70 | 70 | ASTM D1242 |
| Abrasion | 80 | 80 | mm<sup>3</sup>; DIN 53516 |
| Compression Set | 21 % | 21 % | Load = 9.3 MPa (22 hr / 70°C); ASTM D395 Method A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 24.0 J/g | 10.3 BTU/lb | ASTM D3417 |
| CTE, linear | 195 µm/m-°C @Temperature -40.0 - 140 °C |
108 µin/in-°F @Temperature -40.0 - 284 °F |
ASTM D696 |
| Melting Point | 160 °C | 320 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Vicat Softening Point | 132 °C | 270 °F | under 1 daN; ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 5.00e+12 ohm @Temperature 20.0 °C |
5.00e+12 ohm @Temperature 68.0 °F |
65% RH; ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HF1130R PC
- Lubrizol Advanced Materials PEARLTHANE® D16N90UV Thermoplastic Polyurethane Elastomer (discontinued **)
- Gouda Vuurvast CURAS PBK Moldable Refractory Material
- Styron DL 221NA Carboxylated SB
- SABIC Innovative Plastics LNP THERMOCOMP NF001 PC+ABS (Asia Pacific)
- Elastomer Engineering Elastamide 300 Elastomer Modified RIM Nylon 6
- Hexcel® HexPly® F522 Epoxy Resin, 1581 Glass Fabric
- Aclo Accutech ABS ABS834G20L Glass Reinforced
- BASF Ultradur B 4300 G4 BK5110 20% Glass Filled PBT
Copyright © lookpolymers.com All Rights Reserved