Arkema Group Orgalloy® RS 66K15LT Nylon 66 Alloy, Mineral/Impact Grade (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Mineral Filled, Impact Grade
Manufacturer Arkema
Trade Name Orgalloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® RS 66K15LT Nylon 66 Alloy, Mineral/Impact Grade (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties.Mineral filled and impact modified for profile extrusion.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
Water Absorption 2.6 %
2.6 %
Moisture Absorption at Equilibrium 1.1 %
1.1 %
Humidity Absorption
Melt Flow 25 g/10 min

@Load 2.16 kg,
Temperature 275 °C
25 g/10 min

@Load 4.76 lb,
Temperature 527 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.0 MPa
7980 psi
50 mm/min
Elongation at Break 21 %
21 %
Nominal Strain; 50 mm/min
Elongation at Yield 2.9 %
2.9 %
50 mm/min
Tensile Modulus 2.45 GPa
355 ksi
1 mm/min
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 113 µm/m-°C

@Temperature 20.0 °C
62.8 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 89.0 µm/m-°C

@Temperature 20.0 °C
49.4 µin/in-°F

@Temperature 68.0 °F
Melting Point 255 °C
491 °F
10°C/min
Deflection Temperature at 0.46 MPa (66 psi) 202 °C
396 °F
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
Vicat Softening Point 140 °C
284 °F
50°C/hr; 50N
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V