Arkema Group Orgalloy® RS 6015 ES T6L Polyamide Alloy
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® RS 6015 ES T6L Polyamide Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Blow Molding of Technical PartsInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO R1183 |
| Water Absorption | 0.80 % | 0.80 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 23°C / 50% RH; ISO 62 |
| 2.8 % | 2.8 % | in 23°C water; ISO 62 | |
| Melt Flow | 0.50 g/10 min @Load 5.00 kg, Temperature 235 °C |
0.50 g/10 min @Load 11.0 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 81 | 81 | ISO 868 |
| Tensile Strength, Ultimate | 75.0 MPa | 10900 psi | ISO R527 |
| Tensile Strength, Yield | 78.0 MPa | 11300 psi | ISO R527 |
| Elongation at Break | 6.4 % | 6.4 % | ISO R527 |
| Elongation at Yield | 3.2 % | 3.2 % | ISO R527 |
| Flexural Modulus | 2.50 GPa | 363 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| Charpy Impact, Notched | 0.480 J/cm² @Temperature -20.0 °C |
2.28 ft-lb/in² @Temperature -4.00 °F |
ISO 179/Ae |
| 1.36 J/cm² @Temperature 23.0 °C |
6.47 ft-lb/in² @Temperature 73.4 °F |
ISO 179/Ae |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO R1218 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO R75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ISO R75 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® LA-0219-AM LDPE Foam Resin
- Huntsman IROGRAN® A 85 P 4441 TPU-Polyether
- ExxonMobil Exceed™ 1018LA Metallocene Polyethylene Resin (Asia Pacific Grade)
- DuPont™ Kapton® 100ZT Polyimide Film, 25 Micron Thickness
- China Tungsten FeMo60-B Ferro Molybdenum
- Axiall 8610 Moldings & Extrusions Flexible PVC
- Arkema Group Rilsan® ASR 20 Nylon 12, 20% Carbon Fiber Filled (Dry)
- California Fine Wire Nickel Alloy 90 Copper Nickel Resistance Wire
- Asahi Kasei Tenac®-C 4520 Copolymer Acetal Resin
- Compuestos Dominicanos Polycom CE-103165 PVC
Copyright © lookpolymers.com All Rights Reserved