Arkema Group Orgalloy® LE 60LMXV Polyamide 6 Alloy
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® LE 60LMXV Polyamide 6 Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Semi-Flexible grade, Nylon 6 basedTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO R1183 |
| Water Absorption | 0.70 % | 0.70 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 23°C / 50% RH; ISO 62 |
| 5.5 % | 5.5 % | in 23°C water; ISO 62 | |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 61 | 61 | ISO 868 |
| Tensile Strength, Ultimate | 46.0 MPa | 6670 psi | ISO R527 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO R527 |
| Elongation at Break | 280 % | 280 % | ISO R527 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO R527 |
| Modulus of Elasticity | 0.600 GPa | 87.0 ksi | ISO R527 |
| Flexural Strength | 18.0 MPa | 2610 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| Flexural Modulus | 0.500 GPa | 72.5 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| Charpy Impact, Notched | 1.70 J/cm² @Temperature -20.0 °C |
8.09 ft-lb/in² @Temperature -4.00 °F |
After conditioning at 23°C/50%RH; ISO 179/Af |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/Af |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 200 µm/m-°C @Temperature 20.0 - 60.0 °C |
111 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| Melting Point | 220 °C | 428 °F | ISO R1218 |
| Vicat Softening Point | 60.0 °C | 140 °F | 50 N - B method; ISO 306 |
| 195 °C | 383 °F | 10 N - A method; ISO 306 | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
Users viewing this material also viewed the following:
- Overview of materials for Polycarbonate-Urethane
- Lehmann & Voss LUVOCOM® 1105-7751 PEEK, with carbon fiber, easy flowing
- Techmer ES Luriblend® PP GF20 GL2 BK 20% Glass Filled
- SABIC Innovative Plastics NORYL NC220 PPE+HIPS (Asia Pacific)
- A. Schulman POLYBATCH™ Red 5170 Concentrate Based In Polyethylene
- Formosa Plastics Formolon® 40 PVC
- EMS-Grivory Grivory® HT2V-3H LF PA*-GF30
- CTC X-PRO CTC PP 3020 Polypropylene Copolymer
- 3M 7690-T Cold Shrink Silicone Rubber Termination Kits QT-III
- BASF Ultramid® TG7S 35% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved