Owens Corning Glass Fiber Reinforced Polyester BMC (Injection), 22 wt.% glass

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS , Polyester (Thermoset) - Rigid
Manufacturer	Owens Corning
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Owens Corning Glass Fiber Reinforced Polyester BMC (Injection), 22 wt.% glass.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyester thermosets are available in many formulations. They can be formulated for good to excellent resistance to acids, weak alkalis, and organic solvents. However, they are not recommended for use with strong alkalis. Data provided by the manufacturer, Owens Corning.

Physical Properties	Metric	English	Comments
Density	1.82 g/cc	0.0658 lb/in³	ASTM D792
Water Absorption	0.20 %	0.20 %	24 hrs.; ASTM D570

Mechanical Properties	Metric	English	Comments
Hardness, Barcol	68	68
Tensile Strength, Ultimate	33.5 MPa	4860 psi	ASTM D638
Elongation at Break	0.50 %	0.50 %	ASTM D638
Modulus of Elasticity	10.6 GPa	1540 ksi	ASTM D638
Flexural Strength	87.22 MPa	12650 psi	ASTM D790
Flexural Modulus	9.93 GPa	1440 ksi	ASTM D790
Izod Impact, Notched	1.54 J/cm	2.89 ft-lb/in

Thermal Properties	Metric	English	Comments
CTE, linear	11.9 µm/m-°C @Temperature 20.0 °C	6.60 µin/in-°F @Temperature 68.0 °F	ASTM D696
Specific Heat Capacity	1.26 J/g-°C	0.300 BTU/lb-°F
Thermal Conductivity	0.697 W/m-K	4.84 BTU-in/hr-ft²-°F	ASTM C177
Deflection Temperature at 1.8 MPa (264 psi)	260 °C	500 °F	ASTM D648
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Dielectric Constant	4.2 @Frequency 60 Hz	4.2 @Frequency 60 Hz	ASTM D150
Dielectric Strength	14.8 kV/mm	375 kV/in	ASTM D149
Arc Resistance	190 sec	190 sec	ASTM D495