Material Notes:

Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: High Adhesive Strength Bonding: Graphite, Carbon Principal Use: Structures, Molds Graphi-Bond™ 551-RN is exported only as a 2-component system due to shelf life considerations.

Physical Properties	Metric	English	Comments
Density	1.45 - 1.50 g/cc	0.0524 - 0.0542 lb/in³

Mechanical Properties	Metric	English	Comments
Impact Test	40.7 J	30.0 ft-lb	Torque Strength; curing at 1000°F

Thermal Properties	Metric	English	Comments
CTE, linear	7.38 µm/m-°C	4.10 µin/in-°F
Maximum Service Temperature, Inert	2980 °C	5400 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	2.95 kV/mm	75.0 kV/in

Processing Properties	Metric	English	Comments
Processing Temperature	40.0 - 90.0 °C	104 - 194 °F	Application Temp
Cure Time	120 min @Temperature 129 °C	2.00 hour @Temperature 265 °F	Step 1, preceeded by 1-4 hour air set
	120 min @Temperature 260 °C	2.00 hour @Temperature 500 °F	Step 2
Shelf Life	6.00 Month @Temperature -1.11 - 23.9 °C	6.00 Month @Temperature 30.0 - 75.0 °F

Descriptive Properties	Value	Comments
Acid Resistance	Good	after curing at 700°F for 2 hours
Alkali Resistance	Good	after curing at 700°F for 2 hours
Color	Black
Moisture Resistance	Excellent	after curing at 700°F for 2 hours
Solvent	Ethanol
Thinner	Ethanol