- Aremco Ceramabond™ 600-N High Temperature Ceramic Adhesive/Paste, Alumino-Silica Filled
Aremco Ceramabond™ 600-N High Temperature Ceramic Adhesive/Paste, Alumino-Silica Filled
| Category | Ceramic , Oxide , Aluminum Oxide , Silicon Oxide |
| Manufacturer | Aremco |
| Trade Name | Ceramabond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Ceramabond™ 600-N High Temperature Ceramic Adhesive/Paste, Alumino-Silica Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aremco Ceramabond™ 600-N High Temperature Ceramic Adhesive/Paste, Alumino-Silica Filled
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.00 - 2.05 g/cc | 0.0723 - 0.0741 lb/in³ | |
| Volatile Organic Compounds (VOC) Content | 0.000 g/l | 0.000 g/l | |
| Viscosity | 5000 - 15000 cP | 5000 - 15000 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Impact Test | 19.0 J | 14.0 ft-lb | Torque Strength; curing at 1000°F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 5.40 µm/m-°C | 3.00 µin/in-°F | |
| Maximum Service Temperature, Air | 1650 °C | 3000 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 7.99 kV/mm | 203 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Application Temp |
| Cure Time | 60.0 min @Temperature 177 °C |
1.00 hour @Temperature 350 °F |
Step 2 |
| 120 min @Temperature 93.3 °C |
2.00 hour @Temperature 200 °F |
Step 1, preceeded by 1-4 hour air set | |
| Shelf Life | 6.00 Month @Temperature 4.44 - 32.2 °C |
6.00 Month @Temperature 40.0 - 90.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Good | after curing at 700°F for 2 hours |
| Alkali Resistance | Good | after curing at 700°F for 2 hours |
| Color | Tan | |
| Moisture Resistance | Excellent | after curing at 700°F for 2 hours |
| Solvent | Water | |
| Thinner | 600-T |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C4220K PC+ABS (Asia Pacific)
- Ravago Manufacturing Americas Hybrid S555 ABS + Polycarbonate Alloy
- Mitsubishi Hostaphan® WN, 350 micron Nominal Thickness Translucent White Polyethylene Terephthalate Film
- DuPont Appeel® LSR11D542 Lidding Sealant Resin
- Universal Wire Works Inconel 718 (AMS 5832) Filler Metal
- Total HDPE HD 6081 High Density Polyethylene - Injection Molding
- Dow 6D83K Polypropylene Random Copolymer Resin
- Aremco Pyro-Paint™ 634-AL High Temperature Refractory Coating
- Hexion Bakelite™ PF 8052 Phenolic Formaldehyde Resin, Resistant to High Temperatures (discontinued **)
Copyright © lookpolymers.com All Rights Reserved