SABIC Innovative Plastics ULTEM 3452 PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 3452 PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
45% Glass fiber and mineral filled, enhanced flow Polyetherimide (Tg 217C) with enhanced dimensional stability. Resin is RoHS compliant. UL94 V0 and 5VA listing in recognized colors.
Physical Properties Metric English Comments
Density 1.66 g/cc
0.0600 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0025 cm/cm
0.0025 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 8.0 g/10 min

@Load 5.00 kg,
Temperature 360 °C
 8.0 g/10 min

@Load 11.0 lb,
Temperature 680 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
50 mm/min; ISO 527
Elongation at Break 1.5 %
1.5 %
50 mm/min; ISO 527
Tensile Modulus 12.5 GPa
1810 ksi
1 mm/min; ISO 527
Flexural Strength 150 MPa
21800 psi
2 mm/min; ISO 178
Flexural Modulus 12.0 GPa
1740 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
80*10*4; ISO 180/1U
13.0 kJ/m²

@Temperature -30.0 °C
 6.19 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 1.40 J/cm²
6.66 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
1.40 J/cm²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 19.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 10.6 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 36.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 20.0 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 207 °C
405 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 205 °C
401 °F
Rate B/50; ISO 306
205 °C
401 °F
Rate B/120; ISO 306
Glass Transition Temp, Tg 217 °C
423 °F
Flammability, UL94 V-0

@Thickness 0.770 mm
 V-0

@Thickness 0.0303 in
 UL 94
5VA

@Thickness 3.00 mm
 5VA

@Thickness 0.118 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
 3.6

@Frequency 1.00e+6 Hz
 IEC 60250
3.7

@Frequency 50.0 - 60.0 Hz
 3.7

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
 406 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
Dissipation Factor 0.010

@Frequency 50.0 - 60.0 Hz
 0.010

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 125 V
125 V
IEC 60112