Aremco Ceramabond™ 552 High Temperature Ceramic Adhesive/Paste, Alumina Filled
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Aremco |
| Trade Name | Ceramabond™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Ceramabond™ 552 High Temperature Ceramic Adhesive/Paste, Alumina Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: Good Adhesion to Metals Bonding: Ceramic to Ceramic, Ceramic to Metal Principal Use: Low CTE Metals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 - 2.20 g/cc | 0.0686 - 0.0795 lb/in³ | |
| Volatile Organic Compounds (VOC) Content | 0.000 g/l | 0.000 g/l | |
| Viscosity | 53000 - 73000 cP | 53000 - 73000 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Impact Test | 70.5 J | 52.0 ft-lb | Torque Strength; curing at 1000°F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.74 µm/m-°C | 4.30 µin/in-°F | |
| Maximum Service Temperature, Air | 1650 °C | 3000 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 6.81 kV/mm | 173 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Application Temp |
| Cure Time | 120 min @Temperature 93.3 °C |
2.00 hour @Temperature 200 °F |
Step 1, preceeded by 1-4 hour air set |
| 120 min @Temperature 260 °C |
2.00 hour @Temperature 500 °F |
Step 2 | |
| Shelf Life | 6.00 Month @Temperature 4.44 - 32.2 °C |
6.00 Month @Temperature 40.0 - 90.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Good | after curing at 700°F for 2 hours |
| Alkali Resistance | Good | after curing at 700°F for 2 hours |
| Color | White | |
| Moisture Resistance | Excellent | after curing at 700°F for 2 hours |
| Solvent | Water | |
| Thinner | 552-T |
Users viewing this material also viewed the following:
- Nye Lubricants 402 (SO) Synthetic Oil
- Polykemi AB POLYfill PPH T8038 Polypropylene Homopolymer, Mineral Reinforced
- Shandong Rike Chemical HELIâ„¢ HG-60 PVC Processing Aid Series (PA)
- SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Europe-Africa-Middle East)
- Silberline Sparkle Silver® 3334-AR
- DSM Akulon® K224-HG6 (Dry) 30% Glass Reinforced Nylon 6 (North America)
- CMW® ELKONITE® 7065 Infiltrated Molybdenum Silver contact material ASTM B662 Table 1, Class A1
- Dow Corning 5604 Performance Modifier
- Loctite® Durabond® E-90FL Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved