Aremco Aremco-Bond™ 2310 High Performance Epoxide
| Category | Polymer , Adhesive , Thermoset , Epoxy |
| Manufacturer | Aremco |
| Trade Name | Aremco-Bond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Aremco-Bond™ 2310 High Performance Epoxide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ceramic-Filled, 1:1, High Lap Shear and Peel Strength, Autoclavable.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | |
| Viscosity | 45000 cP | 45000 cP | Mixed Viscosity |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 78 | 78 | |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Shear Strength | 32.9 MPa | 4770 psi | ASTM D1002-94 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 77.4 µm/m-°C @Temperature 20.0 °C |
43.0 µin/in-°F @Temperature 68.0 °F |
|
| Maximum Service Temperature, Air | 163 °C | 325 °F | |
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |
| Shrinkage | 0.10 % | 0.10 % | Cure Shrinkage |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+13 ohm-cm | 3.00e+13 ohm-cm | |
| Dielectric Constant | 4.28 @Frequency 1000 Hz |
4.28 @Frequency 1000 Hz |
|
| Dielectric Strength | 16.1 kV/mm | 410 kV/in | |
| Dissipation Factor | 0.40 | 0.40 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 65.6 °C |
2.00 hour @Temperature 150 °F |
Recommended Cure |
| 2880 min @Temperature 23.0 °C |
48.0 hour @Temperature 73.4 °F |
Alternate Cure | |
| Pot Life | 45.0 min @Temperature 25.0 °C |
45.0 min @Temperature 77.0 °F |
100 gm mass |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical Resistance | Good | |
| Color | Black | |
| Mix Ratio By Weight | 1:1 | resin:hardener |
Users viewing this material also viewed the following:
- Polystrand ThermoPro™ IE7011X ECR X-Ply Cross-Ply Polypropylene-Glass Composite
- Asahi Kasei Tenac® 2013A Acetal Homopolymer, UV Stabilized (discontinued **)
- LG Chemical LUPOY RF3208F PC, Halogen Free Flame Retardance
- Solvay Specialty Polymers AvaSpire® AV-650 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber
- SABIC Innovative Plastics Xenoy® XD1507S PBT+PC (Europe-Africa-Middle East)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR MBT
- Azoty Tarnow™ Tarnamid® T-30 MS Polyamide 6 - Natural
- Solvay Specialty Polymers Solef® 1008 PVDF Homopolymer (discontinued **)
- Overview of materials for Nylon 6, Film Grade
- Overview of materials for Cellulose Acetate, Molded
Copyright © lookpolymers.com All Rights Reserved