Ametek Ultra 304L P/M Stainless Steel, Sintered from 6.38 g/cc Green Density

Category	Metal , Ferrous Metal , Stainless Steel , T 300 Series Stainless Steel
Manufacturer	Ametek
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ametek Ultra 304L P/M Stainless Steel, Sintered from 6.38 g/cc Green Density.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ametek's patented Ultra Stainless Steels™ are produced by alloying the conventional austenitic compositions with a small amount of a copper-nickel-tin alloy. This results in a marked improvement in corrosion resistance, while other properties are comparable to the conventional counterparts.Mechanical property data below is from samples lubricated with 1% Acrawax C and pressed at 40 tsi. Green strength 1100 ksi. Specimens were delubricated in air for 20 min. at 950°F (510°C), then sintered in dissociated ammonia for 30 min. at 2100°F (1149°C) and cooled in the water jacketed furnace cooling zone. Dimensional change from die size -0.09%.Information provided by Ametek Specialty Metal Products.

Physical Properties	Metric	English	Comments
Density	6.41 g/cc	0.232 lb/in³

Mechanical Properties	Metric	English
Hardness, Rockwell B	47	47
Tensile Strength, Ultimate	290 MPa	42100 psi
Tensile Strength, Yield	230 MPa	33400 psi
Elongation at Break	4.1 %	4.1 %

Component Elements Properties	Metric	English	Comments
Carbon, C	0.020 %	0.020 %
Chromium, Cr	19 %	19 %
Copper, Cu	0.80 %	0.80 %
Iron, Fe	66 %	66 %	as balance
Manganese, Mn	0.20 %	0.20 %
Nickel, Ni	11 %	11 %
Phosphorous, P	0.010 %	0.010 %
Silicon, Si	0.80 %	0.80 %
Sulfur, S	0.010 %	0.010 %
Tin, Sn	2.0 %	2.0 %