Aleris Alustar H136 Aluminum Alloy

Category	Metal , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer	Aleris
Trade Name	Alustar
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Aleris Alustar H136 Aluminum Alloy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Close in composition to AA5059. Used in defense and mining shielding applications for protection against ballistics and blasts. H136 has a higher elongation than H131 and so provides better protection against mining blasts.

Physical Properties	Metric	English	Comments
Density	2.66 g/cc	0.0961 lb/in³	Aluminum 5083

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	324 MPa @Thickness 50.83 - 76.2 mm	47000 psi @Thickness 2.001 - 3.00 in
	359 MPa @Thickness 12.7 - 50.8 mm	52100 psi @Thickness 0.500 - 2.00 in
	365 MPa @Thickness 6.35 - 12.7 mm	52900 psi @Thickness 0.250 - 0.499 in
Tensile Strength, Yield	269 MPa @Strain 0.200 %, Thickness 6.35 - 12.7 mm	39000 psi @Strain 0.200 %, Thickness 0.250 - 0.499 in
	269 MPa @Strain 0.200 %, Thickness 12.7 - 50.8 mm	39000 psi @Strain 0.200 %, Thickness 0.500 - 2.00 in
	269 MPa @Strain 0.200 %, Thickness 50.83 - 76.2 mm	39000 psi @Strain 0.200 %, Thickness 2.001 - 3.00 in
Elongation at Break	>= 10 % @Thickness 6.35 - 12.7 mm	>= 10 % @Thickness 0.250 - 0.499 in
	>= 10 % @Thickness 12.7 - 50.8 mm	>= 10 % @Thickness 0.500 - 2.00 in
	>= 10 % @Thickness 50.83 - 76.2 mm	>= 10 % @Thickness 2.001 - 3.00 in

Component Elements Properties	Metric	English
Aluminum, Al	93 %	93 %
Chromium, Cr	<= 0.30 %	<= 0.30 %
Copper, Cu	<= 0.40 %	<= 0.40 %
Iron, Fe	<= 0.50 %	<= 0.50 %
Magnesium, Mg	5.0 - 6.0 %	5.0 - 6.0 %
Manganese, Mn	0.60 - 1.2 %	0.60 - 1.2 %
Silicon, Si	<= 0.50 %	<= 0.50 %
Titanium, Ti	<= 0.20 %	<= 0.20 %
Zinc, Zn	0.40 - 1.5 %	0.40 - 1.5 %
Zirconium, Zr	0.050 - 0.25 %	0.050 - 0.25 %