Advanced Polymer Alloys DURACRYN 8070 NC Thermoplastic Rubber
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) |
| Manufacturer | APA - Advanced Polymer Alloys |
| Trade Name | DURACRYN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Advanced Polymer Alloys DURACRYN 8070 NC Thermoplastic Rubber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Advanced Polymer Alloys
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D471; ISO 2781; DIN 53479 |
| Viscosity | 300000 cP @Shear Rate 300 1/s, Temperature 190 °C |
300000 cP @Shear Rate 300 1/s, Temperature 374 °F |
ASTM D3835 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 | 69 | ASTM D2240; ISO 48; DIN 53505 |
| Tensile Strength, Ultimate | 14.5 MPa | 2100 psi | ASTM D412; ISO 37; DIN 53504 |
| 15.20 MPa | 2205 psi | After 7 days at 257°F (125°C); ASTM D573; ISO 188; DIN 53508 | |
| Elongation at Break | 440 % | 440 % | ASTM D412; ISO 37; DIN 53504 |
| 440 % | 440 % | After 7 days at 257°F (125°C); ASTM D573; ISO 188; DIN 53508 | |
| 100% Modulus | 0.00386 GPa | 0.560 ksi | ASTM D412; ISO 37; DIN 53504 |
| 0.00514 GPa | 0.745 ksi | After 7 days at 257°F (125°C); ASTM D573; ISO 188; DIN 53508 | |
| Graves Tear Strength | 38.6 kN/m @Temperature 23.9 °C |
220 pli @Temperature 75.0 °F |
Die C; ASTM D624; DIN 53507 |
| Compression Set | 15 % | 15 % | After 22 Hr at 75°F (24°C); ASTM D395; ISO 815; DIN 53517 |
| 56 % @Temperature 70.0 °C |
56 % @Temperature 158 °F |
22 hrs.; ASTM D395; ISO 815; DIN 53517 | |
| 65 % @Temperature 100 °C |
65 % @Temperature 212 °F |
22 hrs.; ASTM D395; ISO 815; DIN 53517 | |
| Tensile Set | 9.0 % | 9.0 % | ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Clash Berg Stiffness Temperature | -27.0 °C | -16.6 °F | At 10,000 psi; ASTM D1043 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 177 °C | 350 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fluid Resistance - Volume Change, % (ASTM D471) | -24 | After 7 Days in IRM 903 Oil No.3 at 212°F (100°C) |
| -33 | After 7 Days in ASTM Oil No.1 at 212°F (100°C) | |
| -9 | After 7 Days in ASTM Ref. Fuel No. B at 75°F (24°C) |
Users viewing this material also viewed the following:
- Plansee MW30 Molybdenum-Tungsten
- PTS Tristar® PC-10FRN (V) 15 MFI, 5VA, Flame Retardant, UV Stabilized Polycarbonate With Release
- IDI Composites 46-12 Thermoset Polyester, Molding
- Teknor Apex APEX® 130 Polyvinyl Chloride, Flexible
- Unipetrol PE HD LITEN® FB 75 HDPE
- Polyplastics TOPAS® 6017 Cyclic Olefin Copolymer (COC) (Asia/Pacific Grade)
- Polyram RamClean™ 101 Purging Agent
- Dow Engage® 8107 Polyolefin Elastomer
- DuPont Performance Polymers Hypalon® 30 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound (discon
- MF-5040 Polyurethane-based Biomedical Elastomer
Copyright © lookpolymers.com All Rights Reserved