Adell ER-18 Homopolymer Polypropylene, 40% Glass Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler |
| Manufacturer | Adell Plastics, Inc. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adell ER-18 Homopolymer Polypropylene, 40% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Adell Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 60 | 60 | ASTM D785 |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Ultimate | 96.5 MPa | 14000 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 148 MPa | 21500 psi | ASTM D790 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D256 |
| Gardner Impact | 0.300 J | 0.221 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 182 °C | 360 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 331 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- MV Labs AL700 Al(NO3)3.9H2O Aluminum nitrate nonahydrate
- ExxonMobil Escorene® LD-129 MDPE Cast Overwrap Film Resin (discontinued **)
- KKPC KOSYN 1712G Styrene Butadiene Rubber
- Multibase Multi-Flex® A 5001 E LC Black TPE Thermoplastic Elastomer
- Shandong Dongyue Polymer DF-302 PTFE Aqueous Dispersion 60%
- ChevronTexaco Torque Fluid
- BASF Ultramid® 8202C HS PA6 (Conditioned)
- Aremco Corr-Paint™ CP5000 High Temperature Protective Coating Inorganic, Zinc Filled
- SABIC Innovative Plastics Lexan® ML6230 PC Copolymer
- Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved