- Adell ER-16 Homopolymer Polypropylene, 30% Glass Reinforced
Adell ER-16 Homopolymer Polypropylene, 30% Glass Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Adell Plastics, Inc. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adell ER-16 Homopolymer Polypropylene, 30% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Adell Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 60 | 60 | ASTM D785 |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 5.90 GPa | 856 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.30 J/cm | 8.06 ft-lb/in | ASTM D256 |
| Gardner Impact | 0.300 J | 0.221 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 182 °C | 360 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 309 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® DMX9254 PC (Europe-Africa-Middle East)
- Fiberfil® M-1492 BK223 Polypropylene Homopolymer, Glass Reinforced, mica Filled, Chemically coupled
- Lucite International Diakon® TD542 Toughened Acrylic Compound
- Teknor Apex Monprene® MP 1755L3 Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Deep Red 50389 Concentrate Based In Linear Low-Density Polyethylene
- Eurotec® Tecomid® NB40 NL IM PA6, impact modified, natural
- Braskem H 107 Injection Molding Polypropylene
- 3M Nextel™ AF-10 Aerospace Woven Fabric 312
- Bhansali Engineering Abstron SHF-50+M ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved