Aclo Accutech Polypropylene Homopolymer HP0339G10M20CL Glass/Mineral Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass/Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0339G10M20CL Glass/Mineral Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | MD; ASTM D955 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 81 | 81 | ASTM D785 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ASTM D638 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 3.60 GPa | 522 ksi | ASTM D638 |
| Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
| Flexural Modulus | 4.000 GPa | 580.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.750 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 151 °C | 304 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.8 °C | 109 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® LSHF PC (Asia Pacific)
- ExxonMobil Santoprene® 281-87MED Thermoplastic Elastomer (discontinued **)
- Nilit Nilamid A3 H G7 General Purpose 35% Glass Reinforced PA66
- LATI Latilub 87/28-15T K/20 PC, 20% Carbon Fiber Reinforced, PTFE Filled
- Styron XU 31583.00 Carboxylated SB
- Wall Colmonoy WALLEX 50 - Cobalt-Nickel Alloy
- Fainplast Compounds R 220 Rigid PVC, Extrusion
- 3M Cushion-Mount™ E1860H Plus Plate Mounting Tapes with Easy Mount Adhesive and High Plateside Adhesion
- Axiall 8758 Moldings & Extrusions Flexible PVC
- Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved