Aclo Accutech Polypropylene Homopolymer HP0336G20CL Glass Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0336G20CL Glass Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | MD; ASTM D955 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength at Break | 54.0 MPa | 7830 psi | ASTM D638 |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ASTM D638 |
| Flexural Strength | 77.01 MPa | 11170 psi | ASTM D790 |
| Flexural Modulus | 4.000 GPa | 580.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.422 J/cm | 0.790 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/L: 40-60 nm/1-2 um Multi-Walled Carbon Nanotubes
- Park Electrochemical Nelcote® V-341 Polybutadiene Prepreg, 120 E-Glass Reinforced
- PolyOne Geon™ 81510 Polyvinyl Chloride, Rigid (PVC, Rigid)
- PolyOne Edgetek® ES-20GF-15GM/000 Polyethersulfone - 20% Glass Fiber - 15% Milled Glass (discontinued **)
- SSAB Tunnplat Domex® 590XP Extra High-strength Cold-forming Steel
- Samsung Cheil Industries Starex® SR-0340M High Heat Grade ABS
- A. Schulman POLYBATCH™ White LL8855 GP Concentrate Based In LLDPE
- 3M 4296T Adhesion Promoter
- 3M Scotchgard™ 25 Low Maintenance Floor Finish
Copyright © lookpolymers.com All Rights Reserved