Aclo Accutech Polypropylene Homopolymer HP0336G10M20CL Glass/Mineral Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass/Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0336G10M20CL Glass/Mineral Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | MD; ASTM D955 |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 78 | 78 | ASTM D785 |
| Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 3.499 GPa | 507.5 ksi | ASTM D638 |
| Flexural Strength | 69.98 MPa | 10150 psi | ASTM D790 |
| Flexural Modulus | 4.200 GPa | 609.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C | 237 °F |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8103 EP BLK
- PolyOne Geon™ Vinyl Flexible 90048 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Total Lacqrene® 1235 High Impact Polystyrene (discontinued **)
- Lord Adhesives Circalokâ„¢ 6037 Epoxy Adhesive
- Lucent Polymers GPP-240 Homopolymer Polypropylene, 40% Glass Fiber Reinforced, Chemically Coupled
- SABIC Innovative Plastics LNP STAT-KON ZE0039 MODIFIED POLYPHENYLENE (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP RF0069SF PA 66 (Asia Pacific)
- Borealis Xmod™ BG055AI High Stiffness Polypropylene for Injection Molding Applications
- EMS-Grivory Grivory® BM-30 PA6-MD30
- Arlon RBLW401R##-P1 0.040" (1.02 mm) Cured Self-Fusing Silicone Rubber
Copyright © lookpolymers.com All Rights Reserved