Aclo Accutech Polypropylene Homopolymer HP0334M30L Mica Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Mica Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0334M30L Mica Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | MD; ASTM D955 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 58 | 58 | ASTM D785 |
| Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 3.00 GPa | 435 ksi | ASTM D638 |
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Flexural Modulus | 3.099 GPa | 449.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.502 J/cm | 0.940 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.2 °C | 162 °F |
Users viewing this material also viewed the following:
- Rotuba 860H Ethyl Cellulose
- Ravago Manufacturing Americas Hylon® N1040MGHL Nylon 6/6 (Cond)
- Dyna-Purge® E Purging Compound
- Saint-Gobain Fluoroloy® A01 High Performance Seal Material
- Hexcel® HexPly® M36/NC2 180°C (350°F) Curing Epoxy Matrix, Multiaxial Fabric Laminate (NC2)
- DuPont Teijin Films Mylar® OB13AF Polyester Film, 150 Gauge
- Arkema Group Orgalloy® RS 6635 A Polyamide 6.6 Alloy 35% Glass Fiber reinforced
- 3M Scotch® 865 Reinforced Strapping Tape
- Bhansali Engineering Abstron IM-14S ABS Very High Rigidity Injection Molding Grade
- BASF Ultramid® B3M6 Grey 22319 Q94 30% Mineral Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved