Aclo Accutech Polypropylene Copolymer CP0437W10L Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437W10L Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | MD; ASTM D955 |
| Melt Flow | 17 g/10 min | 17 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 65 | 65 | ASTM D785 |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ASTM D638 |
| Elongation at Break | 28 % | 28 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.00 GPa | 145 ksi | ASTM D638 |
| Flexural Strength | 19.0 MPa | 2760 psi | ASTM D790 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Izod Impact, Notched | 2.19 J/cm | 4.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SEAL 1401 Conductive Elastomer
- GRECO ISOTHANE 1690AE Polyether TPU Resin
- Sylvin Technologies 8960-85 Natural PVC Extrusion Compound
- Shakespeare WN-18 diameter 0.2 mm Nylon 6 Monofilament
- Techmer ES HiFill® PA6 GF50 L 50% Glass Filled (Conditioned)
- A. Schulman POLYBATCH™ Silver 70100 Concentrate Based In LDPE
- Dow Corning Z-1212 CHLOROSILANE
- Hippe PF CP 24 Cellulose Paper Reinforced Phenolic Resin - Round, Rolled Tube
- Braskem PB681/59 Blown Film Extrusion Low Density Polyethylene
- Oceanchem Group Magnesium Hydroxide
Copyright © lookpolymers.com All Rights Reserved