Aclo Accutech Polypropylene Copolymer CP0437T30L Talc Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437T30L Talc Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | MD; ASTM D955 |
| Melt Flow | 16 g/10 min | 16 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 50 | 50 | ASTM D785 |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ASTM D638 |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 1.500 GPa | 217.5 ksi | ASTM D638 |
| Flexural Strength | 20.0 MPa | 2900 psi | ASTM D790 |
| Flexural Modulus | 1.900 GPa | 275.5 ksi | ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.90 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 92.2 °C | 198 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.9 °C | 129 °F |
Users viewing this material also viewed the following:
- Nanocyl PLASTICYL™ SEBS1001 SEBS (styrene-ethylene/butadiene-styrene) with 10% Multi-Wall Carbon Nanotubes
- ExxonMobil LD 136.MV Packaging Film Resin (discontinued **)
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
- Iran Petrochemical (PCC) PET BG-821 Polyethylene Terephthalate
- Lehmann & Voss LUVOCOM® PA66/TF/40 Polyamide 66, with PTFE
- Techmer ES HiFill® PA6/6 GF6 HS BK 6% Glass Filled
- SSAB Tunnplat Domex® 600MC HSLA Steel
- ExxonMobil Escorene™ 768.MJ Blown Ethylene Vinyl Acetate Copolymer
- Johnson Matthey HS Platinum Jewelry Alloy
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Carbon Black, N-330 (HAF)
Copyright © lookpolymers.com All Rights Reserved