Aclo Accutech ABS ABS831G40L Glass Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 40% Glass Fiber Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech ABS ABS831G40L Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 77.98 MPa | 11310 psi | ASTM D638 |
| Tensile Strength, Yield | 77.98 MPa | 11310 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 5.799 GPa | 841.1 ksi | ASTM D638 |
| Flexural Strength | 110.0 MPa | 15950 psi | ASTM D790 |
| Flexural Modulus | 10.498 GPa | 1522.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.2 °C | 198 °F |
Users viewing this material also viewed the following:
- DSM Arnitel® EB500 50 Shore D, Blow Molding Grade Copolyester Elastomer (North America) (discontinued **)
- LATI Latamid SP1 G/50 PA 6.10, 50% Glass Fiber Reinforced
- SABIC Innovative Plastics NORYL WCP761 PPE-TPE
- Shandong Dongyue Shenzhou New Material Co CHF100 Perfluorosulfonic Acid Ion-Exchange Resin (PFSA)
- Master Bond EP112FLAN-1 Two Component Flexibilized Heat Curing Epoxy
- Eurostar Starflam M10009AP PP, Flame Retardant, Injection Molding
- Clariant Renol 66B40 Nylon 66, 40% Glass Bead Filled
- Azoty Tarnow™ Tarnamid® T-27 MCS V2 Polyamide 6 - Flame Retarded, Unreinforced
- Arlon 55586XC028 0.0295" Cured/Uncured Silicone Rubber with Fiberglass Substrate
- Zircar Zirconia ZR-CEM Zirconia Cement
Copyright © lookpolymers.com All Rights Reserved