Abatron AboCast 8103-14 One-Component Epoxy

Category	Polymer , Adhesive , Thermoset , Epoxy , Epoxy, Cast, Unreinforced
Manufacturer	Abatron
Trade Name	AboCast
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Abatron AboCast 8103-14 One-Component Epoxy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AboCast 8103-14 is the lowest-viscosity one-component epoxy system with heavy-duty structural and dielectric properties. It is clear and has maximum wetting and penetration. Suggested Uses: Casting; Potting; Encapsulating; Embedding applications where 2-component systems can not be used; Electronic and structural components, patterns, and medical equipment; Coating; Impregnation; Resurfacing; Insulation; Bonding metal, ceramics, glass, and most rigid materials; Assembly; Patching; and Filling.

Physical Properties	Metric	English	Comments
Viscosity	200 cP	200 cP

Mechanical Properties	Metric	English
Hardness, Rockwell M	88	88
Tensile Strength at Break	57.9 MPa	8400 psi
Elongation at Break	5.1 %	5.1 %
Flexural Strength	83.4 MPa	12100 psi
Flexural Modulus	2.28 GPa	330 ksi
Compressive Strength	75.2 MPa	10900 psi

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	79.0 °C	174 °F	Deflection Temp at unknown load

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.04e+14 ohm-cm	3.04e+14 ohm-cm	C 96/23/96
	3.80e+15 ohm-cm	3.80e+15 ohm-cm	"A"
Surface Resistance	1.13e+14 ohm	1.13e+14 ohm	C 96/23/96
	3.93e+15 ohm	3.93e+15 ohm	Cond. A
Dielectric Constant	3.12 @Frequency 1.00e+6 Hz	3.12 @Frequency 1.00e+6 Hz	A
	3.26 @Frequency 60.0 Hz	3.26 @Frequency 60.0 Hz	A

Processing Properties	Metric	English	Comments
Cure Time	60.0 - 120 min @Temperature 150 - 160 °C	1.00 - 2.00 hour @Temperature 302 - 320 °F
	60.0 - 240 min @Temperature 160 - 180 °C	1.00 - 4.00 hour @Temperature 320 - 356 °F	optional
Pot Life	205 min @Temperature 100 °C	205 min @Temperature 212 °F
Shelf Life	5.00 - 8.00 Month	5.00 - 8.00 Month