Abatron AboCast 8-10/Abocure 8-10 Epoxy (discontinued **)

Category	Polymer , Thermoset , Epoxy
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Abatron AboCast 8-10/Abocure 8-10 Epoxy (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

2-part solvent-free dielectric epoxy casting compound.Processing: 100/35 ratio (pbw); Gel time, 1 lb. (2.2 kg): 45 minutes; cures in 6 hours at 25°C (77°F); postcure: 2 hours at 100°C (212°F).Applications: solventless casting, adhesive, and coating.

Physical Properties	Metric	English	Comments
Water Absorption	0.17 %	0.17 %	in 24 hours.
Viscosity Measurement	700	700

Mechanical Properties	Metric	English
Hardness, Shore D	85	85
Tensile Strength, Ultimate	61.36 MPa	8900 psi
Elongation at Break	4.5 %	4.5 %
Flexural Strength	106.87 MPa	15500 psi
Izod Impact, Notched	0.204 J/cm	0.382 ft-lb/in

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	59.0 °C	138 °F	Deflection temperature; load unknown.

Electrical Properties	Metric	English
Electrical Resistivity	<= 1.00e+9 ohm-cm @Temperature 93.3 °C	<= 1.00e+9 ohm-cm @Temperature 200 °F
	3.00e+11 ohm-cm @Temperature 65.6 °C	3.00e+11 ohm-cm @Temperature 150 °F
	2.00e+15 ohm-cm @Temperature 25.0 °C	2.00e+15 ohm-cm @Temperature 77.0 °F
Dielectric Constant	3.68 @Frequency 1e+6 Hz	3.68 @Frequency 1e+6 Hz
Dissipation Factor	0.013 @Frequency 1e+6 Hz	0.013 @Frequency 1e+6 Hz

Processing Properties	Metric	English	Comments
Processing Temperature	25.0 °C	77.0 °F	Curing time: 6 hours; Postcure: 2 hours/100°C (212°F)