Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 8.15 g/cc | 0.294 lb/in³ |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell B | 55 | 55 | Typical Annealed |
Tensile Strength, Ultimate | 482 MPa | 69900 psi | Typical Annealed |
Tensile Strength, Yield | 275 MPa @Strain 0.200 % |
39900 psi @Strain 0.200 % |
Typical; Annealed |
Elongation at Break | 28 % | 28 % | typical in 2"; Annealed |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 4.00 - 4.70 µm/m-°C @Temperature 30.0 - 300 °C |
2.22 - 2.61 µin/in-°F @Temperature 86.0 - 572 °F |
|
6.70 - 7.40 µm/m-°C @Temperature 30.0 - 500 °C |
3.72 - 4.11 µin/in-°F @Temperature 86.0 - 932 °F |
Component Elements Properties | Metric | English | Comments |
---|---|---|---|
Aluminum, Al | 0.0010 % | 0.0010 % | |
Carbon, C | 0.010 % | 0.010 % | |
Chromium, Cr | 0.15 % | 0.15 % | |
Cobalt, Co | 0.0040 % | 0.0040 % | |
Iron, Fe | 58.4 % | 58.4 % | as balance |
Manganese, Mn | 0.50 % | 0.50 % | |
Nickel, Ni | 40.75 % | 40.75 % | |
Phosphorous, P | 0.010 % | 0.010 % | |
Silicon, Si | 0.20 % | 0.20 % | |
Sulfur, S | 0.0070 % | 0.0070 % |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.0000660 ohm-cm | 0.0000660 ohm-cm |