ALM PA 850 Black Nylon 11 SLS Prototyping Polymer
| Category | Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 11 |
| Manufacturer | ALM Advanced Laser Materials |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ALM PA 850 Black Nylon 11 SLS Prototyping Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Advanced Laser Materials (ALM).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.500 g/cc | 0.0181 lb/in³ | ASTM D1895 |
| Density | 1.03 g/cc | 0.0372 lb/in³ | Sintered Part; ASTM D792 |
| Particle Size | 50 µm | 50 µm | Average D50; Laser Diffraction |
| 38 - 78 µm | 38 - 78 µm | Range (D10 to D90); Laser Diffraction | |
| Melt Flow | 26 g/10 min @Load 5.00 kg, Temperature 235 °C |
26 g/10 min @Load 11.0 lb, Temperature 455 °F |
3 min.; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 74 | 74 | ASTM D2240 |
| Tensile Strength at Break | 48.0 MPa | 6960 psi | XY direction; ASTM D638 |
| Tensile Strength, Ultimate | 42.0 MPa | 6090 psi | Z direction; ASTM D638 |
| Elongation at Break | 14 % | 14 % | Z direction; ASTM D638 |
| 51 % | 51 % | XY direction; ASTM D638 | |
| Tensile Modulus | 1.43 GPa | 207 ksi | Z direction; ASTM D638 |
| 1.48 GPa | 215 ksi | XY direction; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 120 µm/m-°C @Temperature 0.000 - 50.0 °C |
66.7 µin/in-°F @Temperature 32.0 - 122 °F |
ASTM E831 |
| 342 µm/m-°C @Temperature 85.0 - 145 °C |
190 µin/in-°F @Temperature 185 - 293 °F |
ASTM E831 | |
| Melting Point | 200 °C | 392 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 188 °C | 370 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.3e+13 ohm-cm | 1.3e+13 ohm-cm | 50% RH; 500V; ASTM D257 |
| Surface Resistance | 4.9e+12 ohm | 4.9e+12 ohm | 50% RH; 500V; ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- LNP Stat-Kon® EC-1008 EM BK8-115 Polyetherimide, Carbon Fiber Reinforcement (discontinued **)
- DSM Akulon® F232-DH Nylon 6 (European Grade) (Cond) (discontinued **)
- Fujipoly Industries WBC Connector
- Ineos L80Z-00 Impact Copolymer Polypropylene
- Shinil Chemical SHINCON PES Electro Conductive Polymer
- BASF Styrodur® 5000 CS Extruded Rigid Polystyrene Foam (Europe)
- ExxonMobil Paxon™ BA53-035 Blow Molding Resin (discontinued **)
- SABIC Innovative Plastics NORYL PX2060 PPE+PS (Europe-Africa-Middle East)
- Ineos H19G-00 Polypropylene Homopolymer
Copyright © lookpolymers.com All Rights Reserved