ALM PA 250 Nylon 12 SLS Prototyping Polymer

Category Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer ALM Advanced Laser Materials
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ALM PA 250 Nylon 12 SLS Prototyping Polymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Highly Recyclable Nylon 12 Laser Sintering Material.Engineered for excellent mechanical properties, part definition and surface finish. Stabilized against thermal degradation resulting in little or no scrap material, with typical virgin refresh rates from 15 to 25%. Good temperature control is required to process this material.Information provided by Advanced Laser Materials (ALM).
Physical Properties Metric English Comments
Bulk Density 0.500 g/cc
0.0181 lb/in³
ASTM D1895
Density 1.01 g/cc
0.0365 lb/in³
Sintered Part; ASTM D792
Particle Size 40 µm
40 µm
Average D50; Laser Diffraction
30 - 50 µm
30 - 50 µm
Range (D10 to D90); Laser Diffraction
Melt Flow 40 g/10 min

@Load 5.00 kg,
Temperature 235 °C
40 g/10 min

@Load 11.0 lb,
Temperature 455 °F
3 min.; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
XY direction; ASTM D638
Tensile Strength, Ultimate 36.0 MPa
5220 psi
Z direction; ASTM D638
Elongation at Break 4 %
4 %
Z direction; ASTM D638
16 %
16 %
XY direction; ASTM D638
Tensile Modulus 1.74 GPa
252 ksi
XY direction; ASTM D638
2.14 GPa
310 ksi
Z direction; ASTM D638
Thermal Properties Metric English Comments
Melting Point 181 °C
358 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 179 °C
354 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C
187 °F
ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 3.1e+14 ohm-cm
3.1e+14 ohm-cm
ASTM D257
Descriptive Properties Value Comments
Color Black
Surface Finish 9 microns