AFE Technologies Cronite Standard Nickel Alloy Castings, No. HR4

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer AFE TEchnologies; North American Cronite
Trade Name Cronite
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF AFE Technologies Cronite Standard Nickel Alloy Castings, No. HR4.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AFE Technologies/North American Cronite, Inc.Composition Notes: Tungsten added but not quantified in composition table.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 500 MPa
72500 psi
As Cast
Tensile Strength, Yield 260 MPa
37700 psi
As Cast
Elongation at Break 8.0 %
8.0 %
As Cast; 5.65 A<sup>0.5</sup>
Rupture Strength 3.80 MPa

@Temperature 1150 °C,
Time 3.60e+7 sec
551 psi

@Temperature 2100 °F,
Time 10000 hour
Stress Rupture
6.00 MPa

@Temperature 1100 °C,
Time 3.60e+7 sec
870 psi

@Temperature 2010 °F,
Time 10000 hour
Stress Rupture
9.30 MPa

@Temperature 1050 °C,
Time 3.60e+7 sec
1350 psi

@Temperature 1920 °F,
Time 10000 hour
Stress Rupture
14.0 MPa

@Temperature 1000 °C,
Time 3.60e+7 sec
2030 psi

@Temperature 1830 °F,
Time 10000 hour
Stress Rupture
20.0 MPa

@Temperature 950 °C,
Time 3.60e+7 sec
2900 psi

@Temperature 1740 °F,
Time 10000 hour
Stress Rupture
28.0 MPa

@Temperature 900 °C,
Time 3.60e+7 sec
4060 psi

@Temperature 1650 °F,
Time 10000 hour
Stress Rupture
39.0 MPa

@Temperature 850 °C,
Time 3.60e+7 sec
5660 psi

@Temperature 1560 °F,
Time 10000 hour
Stress Rupture
52.0 MPa

@Temperature 800 °C,
Time 3.60e+7 sec
7540 psi

@Temperature 1470 °F,
Time 10000 hour
Stress Rupture
70.0 MPa

@Temperature 750 °C,
Time 3.60e+7 sec
10200 psi

@Temperature 1380 °F,
Time 10000 hour
Stress Rupture
93.0 MPa

@Temperature 700 °C,
Time 3.60e+7 sec
13500 psi

@Temperature 1290 °F,
Time 10000 hour
Stress Rupture
Component Elements Properties Metric English Comments
Carbon, C 0.50 %
0.50 %
Chromium, Cr 18 %
18 %
Iron, Fe 27 %
27 %
As Remainder
Manganese, Mn 1.0 %
1.0 %
Nickel, Ni 52 %
52 %
Silicon, Si 1.5 %
1.5 %