A. Schulman ComAlloy Lubrilon® 646 Nylon 6/12, Carbon Fiber/PTFE Reinforced

Category	Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Carbon Fiber Filler
Manufacturer	A. Schulman ComAlloy
Trade Name	Lubrilon®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman ComAlloy Lubrilon® 646 Nylon 6/12, Carbon Fiber/PTFE Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulman product line.

Physical Properties	Metric	English	Comments
Density	1.24 g/cc	0.0448 lb/in³
Linear Mold Shrinkage	0.0010 cm/cm	0.0010 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	106	106	ASTM D785
Tensile Strength, Ultimate	165 MPa	23900 psi	ASTM D638
Elongation at Break	5.0 %	5.0 %	ASTM D638
Flexural Strength	262 MPa	38000 psi	ASTM D790
Flexural Modulus	13.5 GPa	1960 ksi	ASTM D790
Izod Impact, Notched	1.28 J/cm	2.40 ft-lb/in	ASTM D256
Izod Impact, Unnotched	7.26 J/cm	13.6 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	195 - 215 °C	383 - 419 °F
Deflection Temperature at 0.46 MPa (66 psi)	209 °C	408 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	192 °C	378 °F	ASTM D648