PolyOne Geon™ Vinyl Rigid Extrusion L5880 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L5880 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 81 | 81 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 41.9 MPa | 6080 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.62 GPa | 380 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 70.4 MPa | 10200 psi | ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 |
| Izod Impact, Notched | 8.20 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
15.4 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| 11.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
20.6 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| 12.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
22.5 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| Dart Drop Total Energy | 49.8 J/cm @Temperature 23.0 °C |
0.0933 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| 49.8 J/cm @Temperature 23.0 °C |
0.0933 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C @Thickness 3.18 mm |
158 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flame Rating | VTM-0 | UL 94; 0.250 mm, ALL |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Sheet Extrusion | |
| Thermoforming | ||
| PVC Cell Classification | 16344 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- LG Chemical LUMID HI1102A(W) PA6, High Impact
- MetalTek MTEK 25-35Nb Heat Resistant Stainless Steel
- SABIC Innovative Plastics Ultem 1110R PEI
- Sharadaa Ceramics Smart Cast 9 Medium Cement Castables
- SABIC Innovative Plastics LNP THERMOCOMP LC003E PEEK (Asia Pacific)
- Styrolution PS 454N HIPS
- Loctite® 499 General Purpose Ethyl Cyanoacrylate Bonding Adhesive
- Dymax Magnet Bonder™ 2020 Adhesive
- LTL Color Compounds ColorFast® FRPS100 Styrene, High Impact
Copyright © lookpolymers.com All Rights Reserved