A. Schulman ComAlloy Lubrilon® 606 Nylon 6/6, PTFE Filled, Flow Enhanced

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, PTFE Filled
Manufacturer	A. Schulman ComAlloy
Trade Name	Lubrilon®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman ComAlloy Lubrilon® 606 Nylon 6/6, PTFE Filled, Flow Enhanced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulman product line.

Physical Properties	Metric	English	Comments
Density	1.26 g/cc	0.0455 lb/in³
Linear Mold Shrinkage	0.0090 cm/cm	0.0090 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	116	116	ASTM D785
Tensile Strength, Ultimate	59.0 MPa	8560 psi	ASTM D638
Elongation at Break	11 %	11 %	ASTM D638
Flexural Strength	92.0 MPa	13300 psi	ASTM D790
Flexural Modulus	2.70 GPa	392 ksi	ASTM D790
Izod Impact, Notched	0.480 J/cm	0.899 ft-lb/in	ASTM D256
Izod Impact, Unnotched	5.60 J/cm	10.5 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	255 - 275 °C	491 - 527 °F
Deflection Temperature at 0.46 MPa (66 psi)	204 °C	399 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	66.0 °C	151 °F	ASTM D648

Processing Properties	Metric	English	Comments
Processing Temperature	290 °C	554 °F	Approximate middle barrel temperature.