- Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced
- A. Schulman ComAlloy Hiloy® 753 Glass Reinforced, Flow Enhanced, PPS Alloy, UL
A. Schulman ComAlloy Hiloy® 753 Glass Reinforced, Flow Enhanced, PPS Alloy, UL
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 753 Glass Reinforced, Flow Enhanced, PPS Alloy, UL.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Ultimate | 124 MPa | 18000 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 203 MPa | 29400 psi | ASTM D790 |
| Flexural Modulus | 9.30 GPa | 1350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 - 290 °C | 536 - 554 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 271 °C | 520 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 299 - 310 °C | 570 - 590 °F |
Users viewing this material also viewed the following:
- MRC Polymers EMAREXâ„¢ 300 GF43 Nylon 6, 43% Glass Fiber Filled
- Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F)
- Teknor Apex APEX® 4112 Polyvinyl Chloride, Flexible
- Eagle Brass 752 Nickel Silver 18%, 1/2 Hard
- DuPont Teijin Films Teonex® Q51 Polyester Film, 48 Gauge
- 3M AC-132 Adhesion Promoter
- 3M AC-275 Class B-2 Aerospace Sealant
- ArcelorMittal Save 20-15 Electrical Steel
- BASF Ultraform® S2320 003 POM
- Axiall 38901 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved