- A. Schulman ComAlloy Hiloy® 622 Nylon 6/6, Glass Reinforced, UL
A. Schulman ComAlloy Hiloy® 622 Nylon 6/6, Glass Reinforced, UL
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 622 Nylon 6/6, Glass Reinforced, UL.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 125 MPa | 18100 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 208 MPa | 30200 psi | ASTM D790 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ASTM D790 |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.90 J/cm | 7.31 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 469 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 271 - 285 °C | 520 - 545 °F |
Users viewing this material also viewed the following:
- Industeel SUPERELSO® 500 Quenched and Tempered High Strength Steel for Pressure Equipment
- Momentive Performance Materials TUFELâ„¢ II 94305 Low Volatile Extrusion Heat Cured Rubber
- A. Schulman POLYFLAM™ E-17338 22% CACO3 Filled Copolymer Polypropylene
- Dow Corning SYL-OFF® PMCPSL 30 Release Modifier
- DSM Novamid® 1013G30 1 NA PA6-GF30
- Denka REOMER G G8355 Thermoplastic Elastomer, For Injection Molding
- Chosun Refractories CTC-63TD Monolithic Refractories for Ladle and Tundish
- Fainplast Compounds GS 7516 Flexible PVC, Injection Molding for Footwear
- Teknor Apex APEX® 3610-90 Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved