3M Dyneon™ TFX 2035 PTFE (discontinued **)
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | 3M Dyneon™ TFX 2035 PTFE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Applications: Liners, extruded tape, thick wall tubing.Information provided by the Dyneon division of 3M.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.17 g/cc | 2.17 g/cc | ASTM D4895 |
| Particle Size | 500 µm | 500 µm | ASTM D4895 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 32.8 MPa | 4760 psi | ASTM D4895 |
| Elongation at Break | 435 % | 435 % | ASTM D4895 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+18 ohm-cm | 1.00e+18 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Extrusion Pressure | 5200 psi | reduction ratio 400 |
| Reduction Ratio Range | 16-300:1 | Dyneon Method |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® PP 1392 Carbon Black Filled Conductive Thermoplastic Compound
- SABIC Innovative Plastics NORYL SA9000 PPE (Asia Pacific)
- Solvay TECHNYL® A 218HP V30 Black 21N PA66, 30% glass fiber, DRY
- Solvay TECHNYLSTARâ„¢ S 218 V30 PA6, 30% glass filled, Conditioned
- Hexcel® HexPly® M20 266°F (130°C) Curing Epoxy Matrix
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Non-Black, Mistron Vapor
- Covestro Desmopan® DP 1485A Polyurethane
- China Tungsten YG8 Tungsten Carbide
Copyright © lookpolymers.com All Rights Reserved