3M Scotch® Super 88 Vinyl Electrical Tape

Category	Polymer , Tape , Thermoplastic , Vinyl (PVC)
Manufacturer	3M
Trade Name	Scotch®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch® Super 88 Vinyl Electrical Tape.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Scotch® Vinyl Electrical Tape Super 88 is a premium grade, 8.5 mil thick, all-weather vinyl-insulating tape. It is designed to perform continuously in ambient temperatures up to 105°C. The tape is conformable for cold weather application down to -18°C. It has excellent resistance to abrasion, moisture, alkalies, acids, corrosion and varying weather conditions. The combination of elastic backing and aggressive adhesive provides moisture-tight electrical and mechanical protection with minimum bulk. It is UL Listed and is a Canadian Standards Association (CSA) Certified “Insulating Tape”.Information provided by 3M

Physical Properties	Metric	English	Comments
Thickness	216 microns	8.50 mil

Mechanical Properties	Metric	English	Comments
Elongation at Break	100 % @Temperature -18.0 °C	100 % @Temperature -0.400 °F	ASTM D1000
	250 % @Temperature 22.0 °C	250 % @Temperature 71.6 °F	ASTM D1000
Peel Strength	0.307 kN/m @Temperature 2.00 °C	1.75 pli @Temperature 35.6 °F	Adhesion to Steel; ASTM D1000
	0.307 kN/m @Temperature 22.0 °C	1.75 pli @Temperature 71.6 °F	Adhesion to Backing; ASTM D1000
	0.657 kN/m @Temperature -18.0 °C	3.75 pli @Temperature -0.400 °F	Adhesion to Steel; ASTM D1000
	0.657 kN/m @Temperature -18.0 °C	3.75 pli @Temperature -0.400 °F	Adhesion to Backing; ASTM D1000

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	105 °C	221 °F
Minimum Service Temperature, Air	-18.0 °C	-0.400 °F

Electrical Properties	Metric	English	Comments
Insulation Resistance	>= 1.00e+12 ohm	>= 1.00e+12 ohm	ASTM D1000
Dielectric Breakdown	9000 V	9000 V	High Humidity; ASTM D1000
	10000 V	10000 V	Standard condition; ASTM D1000

Descriptive Properties	Value	Comments
Appearance	Black