| Peel Strength |
0.09861 kN/m |
0.5625 pli |
LD Polyethylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| |
0.110 kN/m |
0.625 pli |
LD Polyethylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| |
0.18626 kN/m |
1.0625 pli |
Polycarbonate 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| |
0.27391 kN/m |
1.5625 pli |
LD Polyethylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.307 kN/m |
1.75 pli |
HD Polyethylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.307 kN/m |
1.75 pli |
HD Polyethylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.31773 kN/m |
1.8125 pli |
HD Polyethylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| |
0.3287 kN/m |
1.875 pli |
Polycarbonate 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| |
0.3287 kN/m |
1.875 pli |
LD Polyethylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.351 kN/m |
2.00 pli |
LD Polyethylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.351 kN/m |
2.00 pli |
HD Polyethylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.3725 kN/m |
2.125 pli |
LD Polyethylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.38347 kN/m |
2.1875 pli |
HD Polyethylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.394 kN/m |
2.25 pli |
LD Polyethylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.394 kN/m |
2.25 pli |
Polycarbonate 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.4163 kN/m |
2.375 pli |
Polypropylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.4163 kN/m |
2.375 pli |
Polypropylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.438 kN/m |
2.50 pli |
HD Polyethylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| |
0.438 kN/m |
2.50 pli |
HD Polyethylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.4602 kN/m |
2.625 pli |
Stainless Steel, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.4602 kN/m |
2.625 pli |
Glass, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.4602 kN/m |
2.625 pli |
LD Polyethylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.4602 kN/m |
2.625 pli |
Polypropylene, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| |
0.482 kN/m |
2.75 pli |
Polycarbonate 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.482 kN/m |
2.75 pli |
Polypropylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.482 kN/m |
2.75 pli |
Glass, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.49303 kN/m |
2.8125 pli |
HD Polyethylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.5040 kN/m |
2.875 pli |
Stainless Steel, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.5040 kN/m |
2.875 pli |
Polycarbonate 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.526 kN/m |
3.00 pli |
Glass, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.5478 kN/m |
3.125 pli |
Stainless Steel, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| |
0.5478 kN/m |
3.125 pli |
Glass, 90° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| |
0.58068 kN/m |
3.3125 pli |
Polypropylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.58068 kN/m |
3.3125 pli |
Stainless Steel, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.5916 kN/m |
3.375 pli |
Polypropylene, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| |
0.60259 kN/m |
3.4375 pli |
Polycarbonate 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.614 kN/m |
3.50 pli |
Stainless Steel, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.614 kN/m |
3.50 pli |
Polypropylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.64642 kN/m |
3.6875 pli |
Polycarbonate 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.657 kN/m |
3.75 pli |
Glass, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.66833 kN/m |
3.8125 pli |
Polycarbonate 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.7231 kN/m |
4.125 pli |
Polypropylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.73407 kN/m |
4.1875 pli |
Glass, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.73407 kN/m |
4.1875 pli |
Stainless Steel, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.745 kN/m |
4.25 pli |
Stainless Steel, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.7669 kN/m |
4.375 pli |
Stainless Steel, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| |
0.7669 kN/m |
4.375 pli |
Glass, 180° Peel, Conditioned for 3 days at 49°C; ASTM D3330 |
| |
0.77789 kN/m |
4.4375 pli |
Glass, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |