Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Breakdown | 10000 V @Thickness 1.57 mm |
10000 V @Thickness 0.0620 in |
Cond D-48/50; ASTM D229 S/S |
Industrial Laminates/Norplex NP630 Paper Base Laminate Description: Machining grade with good electrical properties and moisture resistance. Low cold flow with good dimensional stability. Thickness Tested: 0.062", 0.125", and 0.500" |
|||
Dielectric Breakdown | 10000 V @Thickness 1.57 mm |
10000 V @Thickness 0.0620 in |
Cond D-48/50; ASTM D229 S/S |
Industrial Laminates/Norplex NP660 Paper Base Laminate Description: Lower cost paper phenolic NEMA Grade XP. Uses natural kraft paper without pigmented cover sheet. Warm to hot punching. UL listed. Thickness Tested: 0.062", 0.125" & 0.500" |
|||
Dielectric Breakdown | 10000 V @Thickness 1.57 mm |
10000 V @Thickness 0.0620 in |
Cond D-48/50; ASTM D229 S/S |
Industrial Laminates/Norplex NP680 Paper Base Laminate Description: Hot punching grade with electrical properties between NP611 to NP631.Thickness Tested: 0.062", 0.125" & 0.500" |
|||
Dielectric Breakdown | 10000 V @Thickness 1.57 mm |
10000 V @Thickness 0.0620 in |
Cond D-48/50; ASTM D229 S/S |
Industrial Laminates/Norplex NP664 Paper Base Laminate Description: Low cost room temperature punching grade with mechanical and electrical properties similar to NP612. This version is made with pigment cover plies on the surface.Thickness Tested: 0.062.. |
|||
Dielectric Breakdown | >= 10000 V @Temperature 90.0 °C, Time 20.0 sec |
>= 10000 V @Temperature 194 °F, Time 0.00556 hour |
Step-by-step test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe MF GC 21 Woven Glass Cloth Reinforced Melamine Resin - Round, Rolled Tube Used in mechanical and electrical applications. High mechanical strength. Good arc and tracking resistance. Information provided by Hippe. |
|||
Dielectric Breakdown | >= 10000 V @Temperature 90.0 °C, Time 60.0 sec |
>= 10000 V @Temperature 194 °F, Time 0.0167 hour |
Proof test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe MF GC 21 Woven Glass Cloth Reinforced Melamine Resin - Round, Rolled Tube Used in mechanical and electrical applications. High mechanical strength. Good arc and tracking resistance. Information provided by Hippe. |
|||
Dielectric Breakdown | >= 10000 V @Temperature 90.0 °C, Time 20.0 sec |
>= 10000 V @Temperature 194 °F, Time 0.00556 hour |
Step-by-step test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CC 22 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Rolled Tube Used in mechanical and electrical applications. Coarse weave (18-30 threads per cm).Information provided by Hippe. |
|||
Dielectric Breakdown | >= 10000 V @Temperature 90.0 °C, Time 60.0 sec |
>= 10000 V @Temperature 194 °F, Time 0.0167 hour |
Proof test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CC 22 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Rolled Tube Used in mechanical and electrical applications. Coarse weave (18-30 threads per cm).Information provided by Hippe. |
|||
Dielectric Breakdown | >= 10000 V @Temperature 90.0 °C, Time 20.0 sec |
>= 10000 V @Temperature 194 °F, Time 0.00556 hour |
Step -by-step test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CP 42 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical and electrical applications. Good stability of electrical properties when exposed to high relative humidity. Lower mechanical and electrical properties than PF CP 41.Information.. |
|||
Dielectric Breakdown | >= 10000 V @Temperature 90.0 °C, Time 60.0 sec |
>= 10000 V @Temperature 194 °F, Time 0.0167 hour |
Proof test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CP 42 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical and electrical applications. Good stability of electrical properties when exposed to high relative humidity. Lower mechanical and electrical properties than PF CP 41.Information.. |
|||
Dielectric Breakdown | 10000 V @Thickness 0.0508 mm |
10000 V @Thickness 0.00200 in |
ASTM D149 |
DuPont Teijin Films Melinex® ST507 Polyester Film Melinex® ST507 is a slightly hazy, heat stabilized, polyester film. It has good handling characteristics and is recommended for silver circuitry applications, particularly where an adhesion topcoat.. |
|||
Dielectric Breakdown | >= 10000 V @Temperature 90.0 °C, Time 20.0 sec |
>= 10000 V @Temperature 194 °F, Time 0.00556 hour |
Step-by-step test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe EP GC 42 Woven Glass Cloth Reinforced Epoxy Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. Extremely high mechanical strength at elevated temperatures. Very good stability of electrical properties when exposed to high relative .. |
|||
Dielectric Breakdown | >= 10000 V @Temperature 90.0 °C, Time 60.0 sec |
>= 10000 V @Temperature 194 °F, Time 0.0167 hour |
Proof test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe EP GC 42 Woven Glass Cloth Reinforced Epoxy Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. Extremely high mechanical strength at elevated temperatures. Very good stability of electrical properties when exposed to high relative .. |
|||
Dielectric Breakdown | >= 10000 V @Temperature 90.0 °C, Time 20.0 sec |
>= 10000 V @Temperature 194 °F, Time 0.00556 hour |
Step-by-step test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CP 31 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in electrical and mechanical applications. Good stability of electrical properties when exposed to normal relative humidity.Information provided by Hippe. |
|||
Dielectric Breakdown | >= 10000 V @Temperature 90.0 °C, Time 60.0 sec |
>= 10000 V @Temperature 194 °F, Time 0.0167 hour |
Proof test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CP 31 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in electrical and mechanical applications. Good stability of electrical properties when exposed to normal relative humidity.Information provided by Hippe. |
|||
Dielectric Breakdown | >= 10000 V @Temperature 90.0 °C, Time 20.0 sec |
>= 10000 V @Temperature 194 °F, Time 0.00556 hour |
Step-by-step test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CP 43 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical applications and low-voltage electrical applications.Information provided by Hippe. |
|||
Dielectric Breakdown | >= 10000 V @Temperature 90.0 °C, Time 60.0 sec |
>= 10000 V @Temperature 194 °F, Time 0.0167 hour |
Proof test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CP 43 Cellulose Paper Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical applications and low-voltage electrical applications.Information provided by Hippe. |
|||
Dielectric Breakdown | >= 10000 V @Thickness 0.500 mm |
>= 10000 V @Thickness 0.0197 in |
DIN EN 60243 |
CeramTec Rubalit® 708 HP Alumina, 96% (High Performance) Rubalit® 708 HP (High Performance) has been developed from Rubalit® 708S. This material shares the same chemical composition, is produced on the same plant and using the identical production techn.. |